.1 Update is up
-Mag release spring hole corrected, 1mm less deep
-New stipples added
CHAIRMANWON GLOCK V3
Files are not released under any liscense. Commercial use is not premitted without my express consent.
BTC donation address 3QE1kvedKH79Xr3wKZ7nT9hnt7h8LjKh3Q
website can be found at origamifaceshield.com chairmanwon.com or chairmanjuan.com
Consult print orientation PDF for best results
DO NOT USE ANY NOZZLE LARGER THAN .4mm. THERE WILL BE HOLES IN THE PRINT IF YOU DO
Printing Profile Notes
Support X/Y Distance: 1.3mm (stops Cura from supporting stipples)
Use tree supports instead of normal supports (if you are suffering from very long slice times switch back to normal supports, you will waste material compared to trees but the print will be fine)
Enable Z hop on retract
If you are using Prusa Slicer make sure you have Detect Thin Walls set to off
Nozzle: 0.4mm
Layer Height: 0.16mm
Temp: 215-230/60C
Infill: 100%
Walls: 8
Supports: On/full - use a close support interface gap. Your interface gap should not be larger than 0.15mm unless you know what you are doing with your setup.
Cooling: As low as you can get away with for your printer
All other settings can/should be left as default or whatever you know works best with your printing setup.
u/IncreasinglyGreasy · 2022-06-02 17:02:51 UTC · score 138
I’d be interested in seeing how you create the locking mechanism. Any larger than .22lr and even PETG runs the chance of “smushing” the locking surface, gradually increasing headspace. Hell of a project man, I’m excited.
u/Stick_Mag · 2022-06-02 17:19:15 UTC · score 153
.223 or bust
u/Polarkeet · 2022-04-02 17:26:33 UTC · score 14
PETG is stronger and higher temp, but with that strength is more brittleness. I printed the FN40 in PETG. Looked great and solid. Shattered into three pieces on the first shot. Need the impact resistance that PLA+ gives.